100Cr6 vs 23MnB4: 39% composition overlap. Significantly different materials serving different application areas.
100Cr6 vs 23MnB4
Side-by-side chemical composition and mechanical property comparison.
Overview
100Cr6
1.3505
High-carbon chromium bearing steel. The most widely used bearing steel worldwide. Extremely high hardness and wear resistance after heat treatment. Standard for ball and roller bearings, precision shafts, and measuring instruments.
23MnB4
1.5535
Cold-heading boron steel — optimized for cold forming of high-strength fasteners. Boron gives hardenability equivalent to much more expensive Cr-Mo alloys. Supplied spheroidized for cold heading, then quenched+tempered after forming. Property class 10.9 bolts are commonly made from this grade. Used for high-strength bolts (M8-M24), screws, studs, and threaded fasteners for automotive and construction.
| 100Cr6 | 23MnB4 | |
|---|---|---|
| Material Number | 1.3505 | 1.5535 |
| Category | Alloy Steel | Alloy Steel |
| Standard | EN ISO 683-17 | EN 10263-4 |
Chemical composition (wt%)
| Element | 100Cr6 | 23MnB4 | Overlap |
|---|---|---|---|
| C | 0.93–1.05% | 0.2–0.27% | No overlap |
| Si | 0.15–0.35% | 0–0.4% | OK |
| Mn | 0.25–0.45% | 0.8–1.1% | No overlap |
| P | 0–0.025% | 0–0.025% | OK |
Mechanical properties
| Property | 100Cr6 | 23MnB4 | Unit |
|---|---|---|---|
| hardness_hrc | 60–66 | — | HRC |
| hardness_hb | ≤ 223 | — | HB |
| e_modulus | ≥ 210 | ≥ 210 | GPa |
Compatibility Assessment
100Cr6 and 23MnB4 have significantly different compositions (39% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is 100Cr6 the same as 23MnB4?
100Cr6 and 23MnB4 have a 39% composition overlap. They are generally not directly interchangeable.
Can I replace 100Cr6 with 23MnB4?
Generally not recommended. The compositions differ significantly (39% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between 100Cr6 and 23MnB4?
The main differences are in the following elements: C, Mn. 100Cr6 is a Alloy Steel grade, while 23MnB4 is a Alloy Steel grade.
Related Comparisons
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.