13CrMo4-5 vs 30CrMoV9: 27% composition overlap. Significantly different materials serving different application areas.
13CrMo4-5 vs 30CrMoV9
Side-by-side chemical composition and mechanical property comparison.
Overview
13CrMo4-5
1.7335
Low-alloy Cr-Mo steel for elevated-temperature service. Good creep resistance up to 500°C. The standard grade for boiler tubes, headers, superheater tubes, and pressure equipment in power generation. Lower alloy content than 10CrMo9-10.
30CrMoV9
1.7707
THE Cr-Mo-V nitriding steel — Cr 2.3-2.7% forms hard CrN nitrided case (800 HV surface). V addition for secondary hardening. Core QT to UTS 1080-1270 MPa before nitriding at 570-580°C. Used for piston rods, valve stems, cylinder liners, turbine parts, and any component needing extreme surface hardness + fatigue resistance without distortion (low nitriding temp).
| 13CrMo4-5 | 30CrMoV9 | |
|---|---|---|
| Material Number | 1.7335 | 1.7707 |
| Category | Alloy Steel | Alloy Steel |
| Standard | EN 10028-2 | EN 10085 |
Chemical composition (wt%)
| Element | 13CrMo4-5 | 30CrMoV9 | Overlap |
|---|---|---|---|
| C | 0.1–0.17% | 0.26–0.34% | No overlap |
| Si | 0–0.35% | 0–0.4% | OK |
| Mn | 0.4–1% | 0.4–0.7% | OK |
| P | 0–0.025% | — | — |
Mechanical properties
| Property | 13CrMo4-5 | 30CrMoV9 | Unit |
|---|---|---|---|
| tensile_strength | 440–590 | 1080–1270 | MPa |
| yield_strength | ≥ 290 | ≥ 880 | MPa |
| elongation | ≥ 20 | ≥ 10 | % |
Compatibility Assessment
13CrMo4-5 and 30CrMoV9 have significantly different compositions (27% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is 13CrMo4-5 the same as 30CrMoV9?
13CrMo4-5 and 30CrMoV9 have a 27% composition overlap. They are generally not directly interchangeable.
Can I replace 13CrMo4-5 with 30CrMoV9?
Generally not recommended. The compositions differ significantly (27% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between 13CrMo4-5 and 30CrMoV9?
The main differences are in the following elements: C, Cr, Mo. 13CrMo4-5 is a Alloy Steel grade, while 30CrMoV9 is a Alloy Steel grade.
Related Comparisons
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.