15-5PH / X5CrNiCuNb15-5 vs 301: 35% composition overlap. Significantly different materials serving different application areas.
15-5PH / X5CrNiCuNb15-5 vs 301
Side-by-side chemical composition and mechanical property comparison.
Overview
15-5PH / X5CrNiCuNb15-5
1.4545
Martensitic precipitation-hardening stainless steel. Similar to 17-4PH but with better transverse ductility and toughness due to lower delta ferrite. Used for aerospace structural components, nuclear reactor parts, food processing equipment, and high-performance fasteners.
301
1.4310
Austenitic stainless steel with the highest work-hardening rate of all 300-series grades. Lower Cr and Ni (17/7 vs 18/9 for 304) makes it metastable — cold working induces martensite transformation for extreme strength (UTS >1300 MPa in full-hard temper). THE stainless spring steel. Used for stainless springs, washers, clips, structural components requiring high strength + corrosion resistance, and railway car bodies.
| 15-5PH / X5CrNiCuNb15-5 | 301 | |
|---|---|---|
| Material Number | 1.4545 | 1.4310 |
| Category | Stainless Steel | Stainless Steel |
| Standard | AMS 5659 | EN 10088-2 |
Chemical composition (wt%)
| Element | 15-5PH / X5CrNiCuNb15-5 | 301 | Overlap |
|---|---|---|---|
| C | 0–0.07% | 0.05–0.15% | Partial |
| Si | 0–1% | 0–2% | OK |
| Mn | 0–1% | 0–2% | OK |
| P | 0–0.03% | 0–0.045% | OK |
Mechanical properties
| Property | 15-5PH / X5CrNiCuNb15-5 | 301 | Unit |
|---|---|---|---|
| tensile_strength | ≥ 1310 | 520–720 | MPa |
| yield_strength | ≥ 1170 | ≥ 205 | MPa |
| elongation | ≥ 10 | ≥ 45 | % |
Compatibility Assessment
15-5PH / X5CrNiCuNb15-5 and 301 have significantly different compositions (35% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is 15-5PH / X5CrNiCuNb15-5 the same as 301?
15-5PH / X5CrNiCuNb15-5 and 301 have a 35% composition overlap. They are generally not directly interchangeable.
Can I replace 15-5PH / X5CrNiCuNb15-5 with 301?
Generally not recommended. The compositions differ significantly (35% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between 15-5PH / X5CrNiCuNb15-5 and 301?
The main differences are in the following elements: C, Cr, Ni. 15-5PH / X5CrNiCuNb15-5 is a Stainless Steel grade, while 301 is a Stainless Steel grade.
Related Comparisons
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.