17CrNiMo6 vs 22MnB5: 27% composition overlap. Significantly different materials serving different application areas.
17CrNiMo6 vs 22MnB5
Side-by-side chemical composition and mechanical property comparison.
Overview
17CrNiMo6
1.6587
Premium CrNiMo case hardening steel for demanding gear applications. Ni 1.2-1.5% + Mo 0.25-0.35% give excellent core toughness and deep hardenability — suitable for large gears up to 400mm ruling section. Surface HRC 60-63 after carburizing. THE wind turbine gearbox steel. Also used for large industrial gearboxes, mining equipment, and heavy truck transmissions.
22MnB5
1.5528
THE press hardening (hot stamping) boron steel — used in virtually every modern car for B-pillars, bumper beams, and side impact reinforcements. As-delivered: ferritic-pearlitic, UTS 450-750 MPa, formable. After hot stamping + die quenching: fully martensitic, UTS 1300-1650 MPa. Boron (0.002-0.005%) provides critical hardenability at low cost. Usually AlSi or Zn coated to prevent oxidation during austenitizing at 880-950°C.
| 17CrNiMo6 | 22MnB5 | |
|---|---|---|
| Material Number | 1.6587 | 1.5528 |
| Category | Alloy Steel | Alloy Steel |
| Standard | EN 10084 | EN 10083-3 |
Chemical composition (wt%)
| Element | 17CrNiMo6 | 22MnB5 | Overlap |
|---|---|---|---|
| C | 0.15–0.21% | 0.2–0.25% | Partial |
| Si | 0–0.4% | 0–0.4% | OK |
| Mn | 0.5–0.9% | 1.1–1.4% | No overlap |
| P | — | 0–0.025% | — |
Mechanical properties
| Property | 17CrNiMo6 | 22MnB5 | Unit |
|---|---|---|---|
| hardness_hrc | 60–63 | 42–50 | HRC |
| tensile_strength | 1000–1300 | 450–750 | MPa |
| yield_strength | 700–1000 | 300–600 | MPa |
Compatibility Assessment
17CrNiMo6 and 22MnB5 have significantly different compositions (27% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is 17CrNiMo6 the same as 22MnB5?
17CrNiMo6 and 22MnB5 have a 27% composition overlap. They are generally not directly interchangeable.
Can I replace 17CrNiMo6 with 22MnB5?
Generally not recommended. The compositions differ significantly (27% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between 17CrNiMo6 and 22MnB5?
The main differences are in the following elements: C, Mn, Cr. 17CrNiMo6 is a Alloy Steel grade, while 22MnB5 is a Alloy Steel grade.
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.