90MnCrV8 vs A2 / X100CrMoV5: 23% composition overlap. Significantly different materials serving different application areas.
90MnCrV8 vs A2 / X100CrMoV5
Side-by-side chemical composition and mechanical property comparison.
Overview
90MnCrV8
1.2842
Universal cold work tool steel with high carbon and manganese. Oil hardening (AISI O2). Excellent dimensional stability during heat treatment, good wear resistance, and high hardness up to 63 HRC. Easy to machine in annealed condition. Used for blanking and stamping tools, precision punches, shear blades, thread chasers, reamers, measuring gauges, woodworking tools, and cold forming dies. Equivalent to AISI O2.
A2 / X100CrMoV5
1.2363
Air-hardening cold-work tool steel. Combines good wear resistance with excellent dimensional stability during heat treatment (minimal distortion). Used for punching/blanking dies, forming tools, shear blades, gauges, and precision tooling where low distortion is critical.
| 90MnCrV8 | A2 / X100CrMoV5 | |
|---|---|---|
| Material Number | 1.2842 | 1.2363 |
| Category | Tool Steel | Tool Steel |
| Standard | EN ISO 4957 | EN ISO 4957 |
Chemical composition (wt%)
| Element | 90MnCrV8 | A2 / X100CrMoV5 | Overlap |
|---|---|---|---|
| C | 0.85–0.95% | 0.95–1.05% | Partial |
| Si | 0.1–0.4% | 0.1–0.4% | OK |
| Mn | 1.8–2.2% | 0.4–0.8% | No overlap |
| P | ≤ 0.03% | — | — |
Mechanical properties
| Property | 90MnCrV8 | A2 / X100CrMoV5 | Unit |
|---|---|---|---|
| hardness_hb | ≤ 229 | ≤ 229 | HB |
| hardness_hrc | 58–63 | 57–62 | HRC |
| density | ≥ 7.66 | ≥ 7.86 | g/cm3 |
Compatibility Assessment
90MnCrV8 and A2 / X100CrMoV5 have significantly different compositions (23% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is 90MnCrV8 the same as A2 / X100CrMoV5?
90MnCrV8 and A2 / X100CrMoV5 have a 23% composition overlap. They are generally not directly interchangeable.
Can I replace 90MnCrV8 with A2 / X100CrMoV5?
Generally not recommended. The compositions differ significantly (23% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between 90MnCrV8 and A2 / X100CrMoV5?
The main differences are in the following elements: C, Mn, Cr, V. 90MnCrV8 is a Tool Steel grade, while A2 / X100CrMoV5 is a Tool Steel grade.
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.