H13 / X40CrMoV5-1 vs M42: 36% composition overlap. Significantly different materials serving different application areas.
H13 / X40CrMoV5-1 vs M42
Side-by-side chemical composition and mechanical property comparison.
Overview
H13 / X40CrMoV5-1
1.2344
The most widely used hot-work tool steel globally. Excellent combination of hot hardness, toughness, and thermal fatigue resistance. Used for die-casting dies (aluminum, zinc, magnesium), forging dies, extrusion tooling, and hot shear blades.
M42
1.3247
Cobalt super high speed steel — 8% Co for maximum hot hardness (HRC 69 at 550°C). THE HSS for machining superalloys, titanium, and pre-hardened steels where M2 burns out. Mo-series (not W-series like T15). Reaches HRC 68-70 after hardening — among the hardest HSS grades. Also known as HS2-9-1-8 (EN) or SKH59 (JIS). Used for drills, end mills, taps, broaches, and milling cutters for difficult-to-machine materials.
| H13 / X40CrMoV5-1 | M42 | |
|---|---|---|
| Material Number | 1.2344 | 1.3247 |
| Category | Tool Steel | Tool Steel |
| Standard | EN ISO 4957 | EN ISO 4957 |
Chemical composition (wt%)
| Element | H13 / X40CrMoV5-1 | M42 | Overlap |
|---|---|---|---|
| C | 0.35–0.42% | 1.05–1.15% | No overlap |
| Si | 0.8–1.2% | 0–0.65% | No overlap |
| Mn | 0.25–0.5% | 0–0.4% | Partial |
| P | 0–0.03% | 0–0.03% | OK |
Mechanical properties
| Property | H13 / X40CrMoV5-1 | M42 | Unit |
|---|---|---|---|
| hardness_hrc | 44–52 | 68–70 | HRC |
| hardness_hb | ≤ 229 | ≤ 269 | HB |
| e_modulus | ≥ 210 | ≥ 210 | GPa |
Compatibility Assessment
H13 / X40CrMoV5-1 and M42 have significantly different compositions (36% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is H13 / X40CrMoV5-1 the same as M42?
H13 / X40CrMoV5-1 and M42 have a 36% composition overlap. They are generally not directly interchangeable.
Can I replace H13 / X40CrMoV5-1 with M42?
Generally not recommended. The compositions differ significantly (36% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between H13 / X40CrMoV5-1 and M42?
The main differences are in the following elements: C, Si, Mn, Cr. H13 / X40CrMoV5-1 is a Tool Steel grade, while M42 is a Tool Steel grade.
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.