PA6 GF30 vs PA610 (Polyamide 610): 0% composition overlap. Significantly different materials serving different application areas.
PA6 GF30 vs PA610 (Polyamide 610)
Side-by-side chemical composition and mechanical property comparison.
Overview
PA6 GF30
Polyamide 6 with 30% short glass fiber reinforcement — the industry standard for metal replacement in structural injection-molded parts. UTS doubles vs unfilled PA6 (175 vs 80 MPa), stiffness triples (E-Mod 9.5 vs 3.0 GPa), and HDT jumps to 200°C+. The classic materialref.com differentiation case: Ultramid B3WG6 (BASF) = Zytel 73G30 (DuPont) = Durethan BKV 30 (LANXESS) = Akulon K224-G6 (DSM) = Grilon BG-30 (EMS) = Technyl C216 V30 (Domo) — all the same base material. Used for automotive brackets, engine covers, power tool housings, electrical connectors, and structural inserts.
PA610 (Polyamide 610)
Polyamide 610 — partially bio-based (sebacic acid from castor oil). Bridge between PA6 (high moisture) and PA11/PA12 (low moisture). Good balance of stiffness, toughness, and moisture resistance. Lower water absorption than PA6/PA66 (~1.4% saturated vs 8-9%). Used for monofilaments (brush bristles, fishing line), cable ties, automotive fluid-handling, and applications needing PA stiffness with better dimensional stability in humid environments.
| PA6 GF30 | PA610 (Polyamide 610) | |
|---|---|---|
| Material Number | — | — |
| Category | Polymers | Polymers |
| Standard | ISO 10350 | ISO 527-1 |
Chemical composition (wt%) — Pro
| Element | PA6 GF30 | PA610 (Polyamide 610) | Overlap |
|---|---|---|---|
| Polyamide 6 (Base Polymer) | 68–72% | — | — |
| Glass Fiber Reinforcement | 28–32% | — | — |
| Hexamethylenediamine unit | — | 40–50% | — |
| Sebacic Acid unit (bio-based, from castor oil) | — | 50–60% | — |
Mechanical properties — Pro
| Property | PA6 GF30 | PA610 (Polyamide 610) | Unit |
|---|---|---|---|
| Tensile Strength | 170–185 | 55–65 | MPa |
| Elongation | 3–4 | 50–150 | % |
| Elastic Modulus | 8.5–10 | 1800–2200 | GPa |
| Density | |||
| hdt_1_8mpa | |||
| Melting Point | |||
| water_absorption_sat |
Sign up free and get 3 full comparisons immediately.
Sign up free — 3 comparisons/day freeCompatibility Assessment
PA6 GF30 and PA610 (Polyamide 610) have significantly different compositions (0% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is PA6 GF30 the same as PA610 (Polyamide 610)?
PA6 GF30 and PA610 (Polyamide 610) have a 0% composition overlap. They are generally not directly interchangeable.
Can I replace PA6 GF30 with PA610 (Polyamide 610)?
Generally not recommended. The compositions differ significantly (0% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between PA6 GF30 and PA610 (Polyamide 610)?
The main differences are in the following elements: overall alloying content. PA6 GF30 is a Polymers grade, while PA610 (Polyamide 610) is a Polymers grade.
Related Comparisons
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.