EN AW-6082
3.2315THE European structural aluminum alloy — AlSi1MgMn. Highest strength in the 6xxx series (UTS 310 T6). Excellent machinability, good weldability (but HAZ softening), and good corrosion resistance. THE default choice for structural aluminum in Europe — equivalent to what 6061 is in the US. Used for bridges, cranes, transport structures, offshore, and machined components.
International equivalents
| Flag | Standard | Country | Grade | Number | Match |
|---|---|---|---|---|---|
| 🇺🇸 | AA | USA | AA 6082 / UNS A96082 | A96082 | REF |
| 🇪🇺 | EN | Europe | EN AW-6082 (AlSi1MgMn) | 3.2315 | 100% |
Sources: ASTM B221, EN 755-2
Chemical composition comparison (wt%)
Side-by-side: EN AW-6082 (AA) (EN 573-3) vs EN AW-6082 (AlSi1MgMn) (EN)
| Element | EN AW-6082 (AA) | EN AW-6082 (AlSi1MgMn) (EN) | Overlap |
|---|---|---|---|
| Si | 0.7–1.3% | — | — |
| Mn | 0.4–1% | — | — |
| Cr | 0–0.25% | — | — |
| Cu | 0–0.1% | — | — |
| Al | — | — | — |
| Ti | 0–0.1% | — | — |
| Mg | 0.6–1.2% | — | — |
| Fe | 0–0.5% | — | — |
| Zn | 0–0.2% | — | — |
Mechanical properties
T6 (solution treated + artificially aged)
| Property | Value | Unit |
|---|---|---|
| Tensile Strength | 290–340 | MPa |
| Yield Strength | 250–290 | MPa |
| Elongation | 8–10 | % |
| Hardness HB | 90–105 | HB |
| Elastic Modulus | ≥ 70 | GPa |
| Density | ≥ 2.71 | g/cm3 |
Compatibility verdict
EN AW-6082 and EN AW-6082 (AlSi1MgMn): 100% composition match
Close equivalents but NOT identical.
Related materials
EN AW-6082
3.2315High-strength structural aluminium alloy in the Al-Mg-Si family. One of the strongest 6xxx series alloys due to manganese addition. Replaced 6061 in many European applications. Used for trusses, bridges, cranes, transport, scaffolding, and marine applications. Heat treatable (T6/T651).
EN AW-5083
3.3547The highest-strength non-heat-treatable aluminium alloy. Excellent corrosion resistance (especially seawater), good weldability. Standard alloy for shipbuilding, offshore, pressure vessels, cryogenic applications, and armour plate. Not for continuous service above 65°C under stress (SCC risk).
EN AW-2024
3.1355Classic high-strength aerospace aluminium alloy (Al-Cu-Mg). Excellent fatigue resistance — the standard choice for aircraft fuselage skins and wing tension members. Poor corrosion resistance and weldability. Often supplied with Alclad cladding for corrosion protection. In use since 1931.
Not sure which material fits?
🤖 Ask AI Advisor →All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.