PA6 GF50
PA6 with 50% short glass fiber — maximum common GF loading. Very high stiffness (E-Mod ~16 GPa) and strength (UTS ~210 MPa dry) approaching short-fiber-reinforced thermoset territory. Very low elongation (2-3%). High moisture sensitivity retained from PA6 base. Trade names: Ultramid B3EG10 (BASF), Zytel 73G50 (DuPont). Used for structural automotive parts (front-end carriers, pedal brackets), industrial housings, and metal-replacement applications requiring maximum stiffness at minimum cost.
Mechanical properties — Pro
Dry (as molded)
| Property | Value | Unit |
|---|---|---|
| Tensile Strength | ||
| Elongation | ||
| Elastic Modulus | ||
| Density |
Conditioned 50rh
| Property | Value | Unit |
|---|---|---|
| Tensile Strength | ||
| Elastic Modulus |
Sign up free and get 5 full lookups immediately.
Sign up free — 5 lookups/day freeRelated materials
EPDM (Ethylene Propylene Diene Rubber)
Ethylene propylene diene monomer rubber — THE outdoor/weather elastomer. Saturated backbone gives outstanding ozone, UV, and weathering resistance. Excellent resistance to steam, hot water, and polar solvents. NOT resistant to oils/fuels (opposite of NBR). Good electrical insulation. ρ 0.85-1.3 (lightest common rubber). Used for automotive door/window seals, roofing membranes, radiator hoses, HVAC gaskets, and pond liners.
Epoxy/Carbon Fiber (CFRP)
Carbon fiber reinforced epoxy — the benchmark structural composite material. Unidirectional ply: tensile strength 1500–2000 MPa, modulus 120–150 GPa at density 1.55 g/cm³ (5x stronger than steel at 1/5 the weight). Quasi-isotropic layup: UTS ~600 MPa, E ~50 GPa. Autoclave-cured prepreg (aerospace) or infusion/RTM (industrial). Used in aerospace primary structures (fuselage, wings), Formula 1 chassis, bicycle frames, wind turbine blades, pressure vessels (Type IV) and high-end sporting goods. Fiber types: T300, T700, T800, M40J, M55J.
FKM (Fluoroelastomer / Viton)
Fluoroelastomer — THE high-temperature and chemical-resistant rubber. Outstanding resistance to oils, fuels, acids, and solvents at temperatures up to 200°C (short-term 230°C). Fluorine content (64-70%) determines chemical resistance. Trade names: Viton (Chemours), Tecnoflon (Solvay), Dai-El (Daikin). 5-10x more expensive than NBR. Used for aerospace fuel seals, chemical process seals, automotive fuel injector O-rings, semiconductor processing, and any seal exposed to aggressive chemicals at high temperature.
Not sure which material fits?
🤖 Ask AI Advisor →All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.