PA612 (Polyamide 612)
Polyamide 612 — partially bio-based (dodecanedioic acid from palm kernel oil). Even lower moisture absorption than PA610 (~0.9% saturated vs ~1.4%). Better dimensional stability than PA6/PA66 in humid environments. Trade names: Zytel 151/158 (DuPont), Vestamid D (Evonik). Used for precision gears, cable ties, fuel system components, and monofilaments. Between PA610 and PA12 in the moisture/stiffness spectrum.
Chemical composition comparison (wt%)
Side-by-side: PA612 (Polyamide 612) (COMPOSITION) (ISO 1874) vs ASTM
| Element | PA612 (Polyamide 612) (COMPOSITION) | ASTM | Overlap |
|---|---|---|---|
| Hexamethylenediamine unit | 35–45% | — | — |
| Dodecanedioic Acid unit | 55–65% | — | — |
Mechanical properties
Dry (as molded)
| Property | Value | Unit |
|---|---|---|
| Tensile Strength | 50–60 | MPa |
| Elongation | 80–200 | % |
| Elastic Modulus | 1700–2100 | MPa |
| Density | 1.06–1.07 | g/cm3 |
| Melting Point | 215–220 | °C |
| water_absorption_sat | 0.8–1 | % |
Related materials
EPDM (Ethylene Propylene Diene Rubber)
Ethylene propylene diene monomer rubber — THE outdoor/weather elastomer. Saturated backbone gives outstanding ozone, UV, and weathering resistance. Excellent resistance to steam, hot water, and polar solvents. NOT resistant to oils/fuels (opposite of NBR). Good electrical insulation. ρ 0.85-1.3 (lightest common rubber). Used for automotive door/window seals, roofing membranes, radiator hoses, HVAC gaskets, and pond liners.
Epoxy/Carbon Fiber (CFRP)
Carbon fiber reinforced epoxy — the benchmark structural composite material. Unidirectional ply: tensile strength 1500–2000 MPa, modulus 120–150 GPa at density 1.55 g/cm³ (5x stronger than steel at 1/5 the weight). Quasi-isotropic layup: UTS ~600 MPa, E ~50 GPa. Autoclave-cured prepreg (aerospace) or infusion/RTM (industrial). Used in aerospace primary structures (fuselage, wings), Formula 1 chassis, bicycle frames, wind turbine blades, pressure vessels (Type IV) and high-end sporting goods. Fiber types: T300, T700, T800, M40J, M55J.
FKM (Fluoroelastomer / Viton)
Fluoroelastomer — THE high-temperature and chemical-resistant rubber. Outstanding resistance to oils, fuels, acids, and solvents at temperatures up to 200°C (short-term 230°C). Fluorine content (64-70%) determines chemical resistance. Trade names: Viton (Chemours), Tecnoflon (Solvay), Dai-El (Daikin). 5-10x more expensive than NBR. Used for aerospace fuel seals, chemical process seals, automotive fuel injector O-rings, semiconductor processing, and any seal exposed to aggressive chemicals at high temperature.
Not sure which material fits?
🤖 Ask AI Advisor →All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.