40CrMnMo7 vs 90MnCrV8: 44% composition overlap. Significantly different materials serving different application areas.
40CrMnMo7 vs 90MnCrV8
Side-by-side chemical composition and mechanical property comparison.
Overview
40CrMnMo7
1.2311
Pre-hardened plastic mold steel — delivered at 28-32 HRC, ready for machining without further heat treatment. The European equivalent of AISI P20. Cr-Mn-Mo composition for good through-hardenability in large sections. THE workhorse mold base material for injection molds, compression molds, and die casting dies. Good machinability, polishability, and photo-etchability. Used for mold frames, large injection molds, blow molds, and structural die components.
90MnCrV8
1.2842
Universal cold work tool steel with high carbon and manganese. Oil hardening (AISI O2). Excellent dimensional stability during heat treatment, good wear resistance, and high hardness up to 63 HRC. Easy to machine in annealed condition. Used for blanking and stamping tools, precision punches, shear blades, thread chasers, reamers, measuring gauges, woodworking tools, and cold forming dies. Equivalent to AISI O2.
| 40CrMnMo7 | 90MnCrV8 | |
|---|---|---|
| Material Number | 1.2311 | 1.2842 |
| Category | Tool Steel | Tool Steel |
| Standard | EN ISO 4957 | EN ISO 4957 |
Chemical composition (wt%)
| Element | 40CrMnMo7 | 90MnCrV8 | Overlap |
|---|---|---|---|
| C | 0.35–0.45% | 0.85–0.95% | No overlap |
| Si | 0.2–0.4% | 0.1–0.4% | OK |
| Mn | 1.3–1.6% | 1.8–2.2% | No overlap |
| P | 0–0.03% | ≤ 0.03% | OK |
Mechanical properties
| Property | 40CrMnMo7 | 90MnCrV8 | Unit |
|---|---|---|---|
| tensile_strength | 900–1050 | — | MPa |
| yield_strength | 700–800 | — | MPa |
| hardness_hrc | 28–32 | 58–63 | HRC |
Compatibility Assessment
40CrMnMo7 and 90MnCrV8 have significantly different compositions (44% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is 40CrMnMo7 the same as 90MnCrV8?
40CrMnMo7 and 90MnCrV8 have a 44% composition overlap. They are generally not directly interchangeable.
Can I replace 40CrMnMo7 with 90MnCrV8?
Generally not recommended. The compositions differ significantly (44% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between 40CrMnMo7 and 90MnCrV8?
The main differences are in the following elements: C, Mn, Cr. 40CrMnMo7 is a Tool Steel grade, while 90MnCrV8 is a Tool Steel grade.
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.