S620QL
1.8927Quenched and tempered fine-grained structural steel with minimum yield strength 620 MPa and guaranteed impact toughness at -40°C (QL designation). Tighter impurity control for low-temperature service. Used for crane booms in cold climates, offshore lifting equipment, and structural applications requiring both high strength and sub-zero toughness.
Mechanical properties
Related materials
C45E
1.1191Unalloyed special steel with controlled chemistry (E grade) and 0.42–0.50% carbon. Tighter P and S limits than standard C45 for improved consistency. The most widely used medium-carbon steel for quenching and tempering. Good balance of strength (620–850 MPa QT) and toughness. Through-hardening up to ø60mm. Surface hardening by induction to HRC 58. Used for shafts, gears, bolts, connecting rods, crankshafts, and general machine parts.
C25E
1.1158Unalloyed special steel with controlled chemistry (E grade) and ~0.25% carbon. Tighter P and S limits (max 0.025%) than standard C25 for improved consistency. Suitable for quenching and tempering to moderate strength levels. Good machinability and weldability. Used for shafts, bolts, transmission parts, crankshafts, and machine components of moderate stress.
C30
1.0528Medium-carbon unalloyed steel with approximately 0.30% carbon. Intermediate strength between C25 and C35. Good machinability and moderate weldability (preheating recommended for thicker sections). Used for moderately stressed structural parts, shafts, bolts, levers, and connecting rods in general mechanical engineering.
Export this comparison as PDF
Professional datasheet with equivalents, composition, and properties. Ready for your QM documentation.
Download PDF — €4.90Included with PRO subscription